Tribological properties of PPS/PA46 polymer blends

Ferhat Yıldırım1, Mustafa Aydın2, Hakan Yetgin3

1Machinery and Metal Technologies Department, Biga Vocational School, Çanakkale Onsekiz Mart University, Çanakkale, Turkey
2Mechanical Engineering Department, Hasan Ferdi Turgutlu Technologie Faculty, Manisa Celal Bayar University, Manisa, Turkey
3Mechanical Engineering Department, Simav Technologie Faculty, Kütahya Dumlupınar University, Kütahya, Turkey

Abstract

In this study, the tribological performance of originally 40 wt.% fiber glass reinforced polyphenylene sulfide (PPS-G), polyamide 46 (PA46) and their blends were studied at dry sliding conditions. The materials were mixed and extruded on the twin screw extruder. The blends were dried and tribological test specimens were manufactured by using the injection machine. Wear tests were performed with the configuration of a polymer pin on a rotating X40CrMoV5-1 steel disc. Test conditions were atmospheric conditions having 60, 90, 120 N loads and 0.5, 1.0, 1.5 m/s sliding speeds. The obtained results proved that the coefficient of friction for PPS-G, PA46 and their blends is decrease while the applied load and sliding speed values are increase. On the other hand, the specific wear rate is in increase while the applied load and sliding speed values are in increase.

Keywords

Fiber Glass Reinforcement; Hybrid Composite; Polyamide 46; Polyphenylene Sulfide; Wear;

Cite this article as: 

Yildirim F, Aydin M, Yetgin H. Tribological properties of PPS/PA46 polymer blends. Res. Eng. Struct. Mater., 2020; 6(3): 271-282.
Share This Article
LinkedIn
X
Facebook
journal cover
News & Upcoming Events